Polymers of unsaturated esters of polyfluoroalkylthioalcohols

ABSTRACT

This invention relates to novel acrylates, methacrylates, fumarates, maleates, citraconates, mesaconates, itaconates, and aconitates of the following structure: ##STR1## where R 1 , R 2  are each C n  H 2 .sbsb.n, where n is 1 to 12 and may be straight chain or branched; 
     R 3  is hydrogen or C n  H 2 .sbsb.n+1, where n is 1 to 12 and may be straight chain or branched; 
     R 4 , r 5  and R 6  are hydrogen, methyl, ##STR2##  PROVIDED THAT AT LEAST ONE OF R 4 , R 5 , and R 6  is hydrogen or methyl; 
     R f  is C p  F 2p+1  or C p  F 2p+1  OC q  F 2q , where p is 3 to 18 (preferably 6 to 12), q is 2 to 8, and the perfluoroalkyl constituent may be branched or straight chain. 
     Addition polymers made from the above unsaturated esters are particularly useful for treating fabrics to make the fabric oil and water repellent.

This is a division of application Ser. No. 657,140, filed on Feb. 11, 1976, now U.S. Pat. No. 4,060,681.

This invention relates to novel acrylated, methacrylates, fumarates, maleates, citraconates, mesaconates, itaconates, and aconitates of the following structure: ##STR3## where

R¹, R² are each C_(n) H_(2n), where n is 1 to 12 and may be straight chain or branched;

R³ is hydrogen or C_(n) H_(2n+1), where n is 1 to 12 and may be straight chain or branched;

R⁴, R⁵ and R⁶ are hydrogen, methyl, ##STR4## AND

R_(f) is C_(p) F_(2p+1) or C_(p) F_(2p+1) OC_(q) F_(2q), where p is 3 to 18 preferably 6 to 12), q is 2 to 8, and the perfluoroalkyl constituent may be branched or straight chain.

Polymers derived from monomers of Formula I have repeating units of the following structure: ##STR5## where R¹, R², R³, R⁴, R⁵, R⁶ and R_(f) are as defined previously.

Monomers of formula 1 are prepared by the reaction of the corresponding alcohols with α,β-unsaturated acids of Formula III, or esters, anhydrides or acid chlorides thereof. ##STR6##

The alcohols, ##STR7## are disclosed in copending application Ser. No. 652,367 filed Jan. 26, 1976, now abandoned, Dear and Brace, which application is here incorporated by reference. The α,β-unsaturated acids of Formula III, or their esters, anhydrides or acid chlorides are available commercially. These are, for example,

    ______________________________________                                         Formula III α,β                                                     Unsaturated Acids                                                                           R.sup.4   R.sup.5  R.sup.6                                        ______________________________________                                         Acrylic acid --H       --H          --H                                        Methacrylic acid                                                                            --H       --H          --CH.sub.3                                 Fumaric acid --COOH    --H          --H                                        Maleic acid  --H       --COOH       --H                                        Mesaconic acid                                                                              --COOH    --H          --CH.sub.3                                 Citranoic acid                                                                              --H       --COOH       --CH.sub.3                                 Itaconic acid                                                                               --H       --H          --CH.sub.2 COOH                            cis Aconitic acid                                                                           --COOH    --H          --CH.sub.2 COOH                            trans Aconitic acid                                                                         --H       --COOH   --CH.sub.2 COOH                                ______________________________________                                    

The novel esters of Formula I are obtained from the designated alcohols and the α,β unsaturated compounds of Formula III by well-known esterification of transesterification procedures. Many Formula III acids have high melting points and are poorly soluble in many common solvents, thus it is often preferable to use the acid chlorides, anhydrides or lower alkyl esters of the acids.

Polymerization of Perfluoroalkyl Monomers of Formula I

Polymers possessing soil repellent properties may be formed from R_(f) -monomers of Formula I. The polymers contemplated by this invention include homopolymers, copolymers with other ethylenically unsaturated monomers, and physical blends of such homopolymers and copolymers together and/or with other polymers.

The Formula I R_(f) -monomers and polymers derived therefrom can be considered to be divided into two distinct classes due to their polymerization behavior.

These two classes are based on polymers derived from acrylates and methacrylates on one hand, as opposed to fumarates, maleates, mesaconates, citraconates, itaconates, and aconitates on the other hand. The latter class of esters tend to homopolymerize much less readily than the acrylates and methacrylates.

Turning to the first class which are acrylates and methacrylates, the polymerization will proceed as follows: ##STR8##

The acrylate and methacrylate monomers are highly reactive and have a greater tendency to form homo- or copolymers. The polymer chain derived from Formula I acrylates or methacrylates will have two R_(f) groups per monomer moiety.

The polymerization of the R_(f) -acrylate and R_(f) -methacrylate monomers is analogous to the polymerization of acrylate and methacrylate monomers, as described in Houben-Weyl, Methoden der Organischem Chemie, Vol. 14/1, p. 1044-1047, (Georg Thieme Verlag, Stuttgart, 1961) or C. E. Schildknecht, Vinyl and Related Polymers, p. 179-255 (John Wiley and Sons, Inc., New York 1952).

In contrast, the second group of polymers derived from R_(f) -fumarates, maleates, mesaconates, citraconates, itaconates and aconitates show a lower tendency toward homopolymerization and form low-molecular weight homopolymers, also called oligomers. They show however a great tendency to form alternating copolymers with certain types of comonomers as outlined later.

The polymer chain derived from R_(f) -fumarates and related di- and triesters contains four R_(f) -groups per monomer moiety as the following example shows: ##STR9##

The polymerization of the R_(f) -fumarate and related di- and triester monomers of Formula I is analogous to the polymerization of alkyl fumarate or maleate monomers, as described in Houben-Weyl, Methoden der Organischem Chemie, Vol. 14/1 (Georg Thime Verlay Stuttgart, 1961) or C. E. Schildknecht, Vinyl and Related Polymers (John Wiley and Sons, Inc., New York, 1952).

The fact that in the novel polymers of Formula II the R_(f) -groups are present in closely packed clusters of 2 or more R_(f) -groups is most important, since the critical free surface energy of polymers with close-packed R_(f) -groups is lower and, consequently, the oil repellency higher than in conventional R_(f) -polymers containing one R_(f) -group per backbone carbon or per monomer moiety.

Although the ease of polymerization will differ between the acrylate and methacrylate type monomers on one hand and the fumarate and related monomers on the other, similar conditions may be employed to obtain the desired polymerization.

Generally polymerization may be carried our in bulk, solution, suspension or emulsion. Solution and emulsion polymerizations are preferred.

In emulsion polymerization, the monomer or monomers to be polymerized are emulsified together in a water solution of a surface active agent to a given monomer concentration of from about 5% to about 50%. Usually the temperature is raised to between 40° C. and 70° C. to effect polymerization in the presence of an added catalyst. A suitable catalyst may be of any one of the commonly known agents for initiating the polymerization of an ethylenically unsaturated compound. The concentration of the catalyst for the polymerization is usually between 0.1% and 2% based upon the weight of the monomers.

Suitable surfactants or emulsifying agents include cationic, anionic or non-ionic types. Since the cationic and non-ionic types can be used in most textile treating baths, they are preferred. The hydrophobic portion of the surfactant may be hydrocarbon or fluorinated hydrocarbon.

Suitable surfactants or emulsifying agents include, for example, non-ionic surfactants in which the hydrophilic group is poly(ethoxy) group and the hydrophobic portion is either a hydrocarbon or a fluorocarbon group such as the ethylene oxide condensates of alkyl phenols, alkanols, alkylamines, alkyl thiols, alkylcarboxylic acids, fluoroalkyl carboxylic acids, fluoroalkyl amines and the like.

Suitable cationic surfactants include for example, quaternary ammonium salts or amine salts containing at least one long chain alkyl, fluoroalkyl or high alkyl substituted benzene or naphthalene group to provide the hydrophobic portion.

Polymerization is preferably carried out for a reaction period adjusted to obtain essentially quantitative conversion of the fluorinated monomer. The optimum reaction time will depend upon the catalyst used and the polymerization temperature and other conditions, but will generally be in the range of from 0.5 to 24 hours.

The polymerization temperature will depend upon the catalyst chosen. In the case of emulsion polymerization in aqueous media, it will generally be in the range of from 20° C. to 90° C. The polymerization is generally most conveniently and preferably carried out at atmospheric pressure wherever possible.

In solution polymerization, the monomer or monomers are dissolved in a suitable solvent such as fluorinated solvents, for example, hexafluoroxylene, trifulorotoluene or mixtures thereof with acetone and/or ethylacetate and polymerized in a reaction vessel using initiators such as azobisisobutyronitrile or other azo initiators at concentrations of 0.1 to 2.0% at 40°-100° C. under nitrogen.

As mentioned, besides homopolymers, valuable copolymers are obtained by polymerization of the foregoing novel perfluorinated monomers with other polymerizable monomers having ethylene unsaturation.

The following types of comonomers are useful in the preparation of copolymers of the novel R_(f) -monomers:

Ethylene and chloro, fluoro- and cyano-derivatives of ethylene such as vinyl chloride, vinylidene chloride, vinyl fluoride, acrylonitrile, methacrylonitrile, tetrafluoroethylene, hexafluoropropylene, acrylate and methacrylate monomers, particularly those with 1 to 12 or 18 carbon atoms in the ester groups such as n-propyl methacrylate, 2-methyl cyclohexyl methacrylate, methyl methacrylate, t-butyl methacrylate, n-butyl methacrylate, methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate, 3-methyl-1-pentyl acrylate, octyl acrylate, tetradecyl acrylate, s-butyl acrylate, 2-ethylhexyl acrylate, 2-methoxyethyl acrylate, and phenyl acrylate; dienes particularly 1,3-butadiene, isoprene, and chloroprene, 2-fluoro-butadiene, 1,1,3-trifluorobutadiene, 1,1,2,3-tetrafluoro butadiene, 1,1,2-trifluoro-3,4-dichlorobutadiene and tri- and pentafluoro butadiene and isoprene; nitrogenvinyl monomers such as vinyl pyridine, N-vinylamides, amides, vinyl succinimide, vinyl pyrrolidone, N-vinyl carbazole and the like; styrene and related monomers which copolymerize readily with the novel esters of this invention such as o-methylstyrene, p-methylstyrene, 3,4-dimethyl styrene, m-ethyl styrene, 2,5-diethyl styrene; vinyl esters, e.g. vinyl acetate, vinyl esters of substituted acids, such as for example, vinyl methoxyacetate, vinyl trimethylacetate, vinyl isobutyrate, isopropenyl butyrate, vinyl lactate, vinyl caprylate, vinyl pelargonate, vinyl myristate, vinyl oleate and vinyl linoleate; vinyl esters of aromatic acids, such as vinyl benzoate; alkyl vinyl-ethers, such as methyl vinyl ether, isopropyl vinyl ether, isopropyl vinyl ether, isobutyl vinyl ether, 2-methoxy ethyl vinyl ether, n-propyl vinyl ether, t-butyl vinyl ether, isoamyl vinyl ether, n-hexyl vinyl ether, 2-ethylbutyl vinyl ether, diisopropylmethyl vinyl ether, 1-methyl-heptyl vinyl ether, n-decyl vinyl ether, n-tetradecyl vinyl ether, and n-octadecyl vinyl ether.

Propylene, butylene and isobutylene are preferred α-olefins useful as comonomers with the novel fluoro monomers of the present invention with straight and branched chain α-olefins useful with up to 10 carbon atoms in the side chain.

Also useful as comonomers with some of the novel monomers of the present invention are vinyl monomers which contain perfluorinated side chains. Examples of such perfluorinated monomers are vinyl ethers of the type disclosed in U.S. Pat. No. 2,732,370, and U.S. Pat. No. 2,828,025; vinyl esters containing fluorinated alkyl groups disclosed in U.S. Pat. No. 2,592,069 and U.S. Pat. No. 2,436,144. Other useful monomers are acrylates and methacrylates and derivatives thereof such as those disclosed in U.S. Pat. No. 2,628,958; U.S. Pat. No. 3,256,230; U.S. Pat. No. 2,839,513; U.S. Pat. No. 3,282,905; U.S. Pat. No. 3,252,932; and U.S. Pat. No. 3,304,278.

Other R_(f) -group-containing monomers useful for copolymerization are fumarates, maleates, itaconates, and other α,β-unsaturated di- and triesters as described in the following application and patents, assigned to the assignee of the instant invention: Ser. No. 720,370, filed Apr. 10, 1968, in the names of Eduard K. Kleiner and Martin Knell; U.S. Pat. No. 3,658,857, issued Apr. 25, 1972 in the names of Eduard K. Kleiner, Martin Knell and Pier Luigi Pacini, U.S. Pat. No. 3,636,085, issued Jan. 18, 1972 in the name of Eduard K. Kleiner, U.S. Pat. No. 3,658,843, issued Apr. 25, 1972 in the name of Eduard K. Kleiner, and U.S. Pat. No. 3,645,985, issued Feb. 29, 1972 in the name of Eduard K. Kleiner and Pier Luigi Pacini.

Of the listed comonomers, the acrylate and methacrylate monomers are the most important comonomers for the novel R_(f) -acrylates and R_(f) -methacrylates, whereas vinyl ethers, vinyl esters, styrenes and α-olefins are the most important comonomers for the novel R_(f) -fumarates and related di- and triesters due to the fact that they form 1:1 alternating copolymers.

As mentioned, it may also be desirable to include a minor amount of other reactive comonomers in order to improve the wash and dry-clean properties of the novel textile finishes obtained according to the practice of this invention. Such monomers act as cross-linking agents during the curing operation. Such reactive comonomers are generally employed in amounts of 0.1% to 2%.

Reactive monomers which may be included are by way of illustration: acrylic acid, methacrylic acid, acrylamide, methacrylmiade, N-methylolacrylamide, 2-hydroxyethyl methacrylate or acrylate, hydroxypropyl acrylates or methacrylates, and t-butylaminoethyl methacrylate, and glycidyl methacrylate. Of the foregoing, N-methylolacrylamide and 2-hydroxyethyl methacrylate are preferred.

Coatings of the homopolymers and copolymers according to the instant invention can be prepared and applied from solvent solutions or from aqueous emulsions. Suitable solvents are fluoroalkanes, fluorochloroalkanes, fluoroalkyl substituted aromatics, alkyl esters of perfluoroalkanoic acids, chlorinated alkanes or aromatics, hydrocarbon aromatics, ketones, esters and ethers. Especially useful as solvents are the fluorinated liquids, and especially α,α,α-trifulorotoluene, otherwise konwn as benzotrifluoride, hexafluoroxylene and mixtures of these with ethyl acetate or acetone and the like. Concentrations of the fluorinated polymers of the instant invention in solvent to provide coatings with effective oil and water repellency properties will generally be of the order of 0.01 to 10% and preferably from 0.1 to 2.0% by weight. Blends of the emulsions of the polymers of this invention with blended emulsions of other polymers and copolymers are particularly useful in textile finishes. The polymers and copolymers are generally of a non-fluorinated type; however, as indicated below other fluorinated polymers and copolymers may be used if desired. Non-fluorinated polymers useful in such blends, include for example, but without limitation, polymers and copolymers of alkyl acrylates and alkyl methacrylates, such as methyl methacrylate, ethyl methacrylate, hexyl methacrylate, and n-octyl methacrylate. A particularly suitable polymer is poly-n-octyl methacrylate. Also useful are polymers and copolymers of acrylic acid, methacrylic acid, styrene, alkyl styrene, butadiene, 2-methyl-1,3-butadiene, 2-chloro-1,3-butadiene; polymers and copolymers of vinyl esters such as vinyl acetate, vinyl butyrate, vinyl laurate, vinyl stearate, vinyl 2-ethyl-hexanoate; polymers and copolymers of vinyl halides and vinylidene halides, such as vinyl chloride, vinylidene chloride, vinyl fluoride, vinylidene fluoride; polymers and copolymers of allyl esters such as allyl propionate, or allyl caprylate; polymers and copolymers of vinyl ketones, such as vinyl methyl ketone, vinyl ethyl ketone, and the like; polymers and copolymers of vinyl ethers such as methyl vinyl ether, cetyl vinyl ether, and the like; polymers and copolymers of acrylamide, methacrylamide, N-methylol acrylamide, N-methylol methacrylamide, N-isopropyl acrylamide, and acrylonitrile and methacrylonitrile.

The polymers of this disclosure possess desirable soil repellency properties. A useful manner of measuring the relative ratings of the polymers is by oil and water repellency ratings. In the examples of the following test procedures were used:

The AATCC oil rating was determined according to Standard Test Method 118-1966 T of the American Association of Textile Chemists and Colorists. Ratings are given from 0 (minimum) to 8 (maximum). A commonly accepted level on soil repellent fabrics in the U.S. is an oil repellency of 4.

Another oil repellency method is the 3-M Oil Test procedure of Grajek and Peterson, Textile Research Journal, April 1962, p. 323.

The AATCC water spray test rating was determined according to Standard Test Method 22-1966 of the American Association of Testile Chemists and Colorists XXVII, 1961, P. 1952 (also designated ASTM-D-583-58). Ratings are given from 0 (minimum) to 100 (maximum).

The polymers in the examples were applied to polyester or polyester-cotton (65%/35%). The polymers were applied to yield a concentration of 0.08 and 0.12% fluorine based on the weight of the fabric. The alcohols ##STR10## are prepared as disclosed in our copending application Ser. No. 652,367, filed Jan. 26, 1976 (now abandoned).

Specific examples of these alcohols are: ##STR11##

To further illustrate the novel aspects of this invention relating to the novel α,β-unsaturated mono, di- and triesters of Formula I and the polymers of Formula II, the following Examples are provided. In the Examples, the temperatures are given in degrees centigrade unless otherwise indicated. Nuclear magnetic resonance data are given in parts per million, referred to the tetramethylsilane signal.

EXAMPLE 1 2,3-Bis(1,1,2,2-Tetrahydroperfluorodecylthio)propyl Methacrylate ##STR12##

2,3-Bis(1,1,2,2-tetrahydroperfluorodecylthio)propan-1-ol (10.16 g; 0.01 mole) was mixed in a 50 ml three neck flask with pyridine (0.83 g; 0.01 mole) and 10 ml methyl ethyl ketone as solvent. The solution was warmed to 70° C. under nitrogen and methacrylyl chloride (1.09 g; 0.0105 mole) over 30 minutes. A white precipitate of pyridine hydrochloride formed, which was removed by filtration after a further one hour at 70° C. The soild was washed two times with 5 ml. acetone and the washings and filtrate combined and stripped to an oil at 40° C. and 15 mm. Hg. The product weighed 10.5 g (96.8% of theory). Final purification was effected by passage through a short column of neutral alumina. Infrared showed bands at 1721 cm⁻¹ (C═O) and 1638 cm⁻¹ (C═C). NMR showed signals at 1.92 ppm (3H) CH₂ ; 1.9-3.5 ppm (11H) CH+CH₂ ; 4.45 ppm (2H) OCH₂ ; 5.6 ppm (1H)=CH trans; 6.1 ppm (1H)=CH cis

Elemental Analysis: Calc'd. for C₂₇ H₁₈ F₃₄ O₂ S₂ : C, 29.90; H, 1.67; F, 59.56. Found C, 30.31; H, 1.78; F, 59.04.

EXAMPLE 2 2,3-Bis(1,1,2,2-Tetrahydroperfluoroalkylthio)propyl Methacrylate ##STR13## (R_(f) =mixture of C₆ F₁₃, C₈ F₁₇ and C₁₀ F₂₁ ratios as described).

In a similar manner 2,3-bis(1,1,2,2-tetrahydroperfluoroalkylthio)propan-1-ol (50 g; 0.0489 mole) (containing 4.0%, C₆ C₆ ; 24.3% C₆ C₈ ; 37.3% C₈ C₈ +C₆ C₁₀ ; 25.5% C₈ C₁₀ ; 6.4% C₁₀ C₁₀ fluorinated chains) reacted with methacrylyl chloride (5.88 g; 0.059 mole) and pyridine (4.91 g; 0.059 mole) in benzene to give the mixed R_(f) -fumarate shown above. The product weighed 30.2 g (59.8% of theory). Infrared showed C═O stretching frequency at 1720 cm⁻¹ and C═C stretching frequency at 1637 cm⁻¹. NMR showed signals at 1.95 ppm (3H) CH₃ ; 2.0-3.2 ppm (11H R_(f) CH₂ CH₂ and SCHCH; 4.35 ppm (2H) OCH₂ ; 5.6 ppm (1H)=CH trans to C═O and 6.1 ppm (1H)=CH cis to C═O.

EXAMPLE 3 Bis[2,3-di(1,1,2,2-Tetrahydroperfluorodecylthio)]propyl]Fumarate ##STR14##

2,3-Bis(1,1,2,2-tetrahydroperfluorodecylthio)propan-1-ol (10.16 g; 0.01 mole) was heated at 140° C., under nitrogen, with fumaryl chloride (0.76 g; 0.005 mole) in 20 ml o-xylene. Upon cooling, a solid product separated. The crude produce was dissolved in 50 ml 1,1,1-trichloroethane and purified by passage through neutral alumina. Obtained 6.8 g (64.4% of theory) m.p. 55°-60°. Infrared showed bands at 1721 cm⁻¹ (C═O) and 1692 cm⁻¹ (C═C). NMR showed signals at 2.0-3.4 ppm (11H) CH and CH₂ ; 4.43 ppm (4H) OCH₂ ; 6.85 ppm (2H)=CH

Elemental Analysis: Calc'd. for C₅₀ H₂₈ F₆₈ O₄ S₄ : C, 28.42; H, 1.34. Found: C, 28.79; H, 1.49.

EXAMPLE 4 Bis[2,3-di(1,1,2,2-Tetrahydroperfluoroalkylthio)propyl]Fumarate ##STR15## Where R_(f) is as defined in Example 2.

In a similar manner 2,3-bis(1,1,2,2-tetrahydroperfluoroalkylthio)propan-1-ol (50 g; 0.049 moles) was converted to 35.2 g fumarate (67.7% yield) by reaction with fumaryl chloride (3.74 g; 0.025 mole) in o-xylene at reflux temperature. The product was a tan, waxy solid, melting over the range 45°-55°.

Infrared showed C═O stretching frequency at 1722 cm⁻¹ and C═C stretching frequency at 1694 cm⁻¹.

EXAMPLE 5 Bis[2,3-di(1,1,2,2-Tetrahydroperfluorodecylthio)propyl]Itaconate ##STR16##

2,3-Bis(1,1,2,2-tetrahydroperfluorodecylthio)propan-1-ol (10 g; 0.098 mole) was mixed with pyridine (0.37 g; 0.047 mole) in 20 ml of heptane, under nitrogen in a three-necked flask. Itaconyl chloride (0.78 g; 0.047 mole) was added at 70° to the above mixture and the reaction was continued, with stirring for 17 hours. A small amount of black tarry material was removed by filtration and the crude product (8.7 g; 87.4% of theory) was isolated by stripping off the heptane under reduced pressure. The itaconate was purified by passage through neutral alumina to obtain a product melting at 45°-55°. Infrared showed C═O stretching frequency at 1725 cm⁻¹ and C═C stretching frequency at 1640 cm⁻¹. NMR showed signals at: 2.0-3.3 ppm (22H) C₈ F₁₇ CH₂ CH₂ SCH and C₈ F₁₇ CH₂ CH₂ SCH₂ ; ##STR17## 6.78 ppm (1H) trans to C═O and 6.38 ppm (1H) cis to C═O.

Elemental Analysis: Calc'd. for C₅₁ H₃₀ F₆₈ O₄ S₄ : C, 28.80; I, 1.42; F, 60.74. Found: C, 28.90; I, 1.57; F, 59.30.

EXAMPLES 6-10

The scope of the invention is further illustrated by the following Examples of unsaturated esters prepared from R_(f) -alcohols by reaction with unsaturated acyl halides.

                                      TABLE I                                      __________________________________________________________________________     Example                                                                             Alcohol or Diol     Acyl Halide                                                                               Product                                    __________________________________________________________________________           ##STR18##          CH.sub.2CHCOCl                                                                             ##STR19##                                 7                                                                                    ##STR20##          CH.sub.2C(CH.sub.3)COCl                                                                    ##STR21##                                 8                                                                                    ##STR22##                                                                                          ##STR23##                                                                                 ##STR24##                                 9                                                                                    ##STR25##                                                                                          ##STR26##                                                                                 ##STR27##                                 10                                                                                   ##STR28##          CHCHCOCl                                                                                   ##STR29##                                 __________________________________________________________________________

example 11 bis[2,3-di(1,1,2,2-Tetrahydroperfluoroalkylthio)propyl] with Vinyl Acetate

Bis[2,3-di(1,1,2,2-tetrahydroperfluoroalkylthio)propyl]fumarate (4.0 g; 0.019 mole), vinyl acetate (0.16 g; 0.0019 mole), azobisisobutyronitrile (0.02 g) and 4 g hexafluoroxylene were sealed in an ampoule under nitrogen and heated for 16 hours at 80° C. The solution then was diluted with 8 g hexafluoroxylene and poured into 240 ml methanol. The precipitated polymer was filtered, washed and vacuum dried, yielding 2.44 g (58.6% yield) of a pale beige powder.

Elemental Analysis: Calc'd.: C, 29.49; H, 1.56; F, 58.75. Found: C, 28.89; H, 1.33 F, 60.21.

EXAMPLE 12 Fumarate Copolymer with Styrene

Using the fumarate of Example 11 and the method described in Example 11, the fumarate was heated with styrene (0.20 g; 0.0019 mole). Work up gave 2.79 g (66.6% yield) of a pale beige powder.

Elemental Analysis: Calc'd.: C, 31.42; H, 1.64; F, 58.27. Found: C, 31.12; H, 1.51; F, 58.40.

EXAMPLE 13 Copolymer of the Fumarate with Vinyl Methyl Ether

Following the procedure of Example 11, the polymerization was carried out with vinyl ether (0.11 g; 0.019 mole). Work up gave 1.89 g (46.2% yield) of a pale beige powder.

Elemental Analysis: Calc'd.: C, 29.32; H, 1.58; F, 59.51. Found: C, 29.14; H, 1.41; F, 60.14.

EXAMPLE 14 Copolymer of the Fumarate with Vinyl Pyrrolidone

Following the procedure of Example 11, the polymerization was carried out with vinyl pyrrolidone (0.21 g; 0.0019 mole). Work up gave 2.74 g (65.1% yield) of a pale beige powder.

Elemental Analysis: Calc'd.: C, 30.24; H, 1.68; F, 58.09; N, 0.63. Found: C, 29.35; H, 1.69; F, 59.56; N, 0.72.

EXAMPLE 15 Homopolymerization of Bis[2,3-di-(1,1,2,2-Tetrahydroperfluoroalkylthio)propyl]Fumarate

Bis[2,3-di(1,1,2,2-tetrahydroperfluoroalkylthio)propyl]fumarate (4.00 g; 0.0019 mole) and benzoyl peroxide (0.01 g) were sealed in an ampoule under nitrogen and heated at 80° C. for 16 hours. The solid polymer was washed with 8 ml acetone, then dissolved in 12 g hexafluoroxylene and finally recovered by precipitation in 240 ml methanol. Filtration and drying gave 2.14 g (53.5% yield) of polymer.

Elemental Analysis: Calc'd.: C, 28.42; H, 1.34; F, 61.15. Found: C, 27.91; H, 1.19; F, 61.66.

EXAMPLE 16 Copolymer of Bis[2,3-di(1,1,2,2-Tetrahydroperfluorodecylthio)propyl]Fumarate and Vinyl-2-Methoxyethylether

Bis[2,3-di(1,1,2,2-tetrahydroperfluorodecylthio)propyl]fumarate (1.90 g; 0.0009 mole), vinyl-2-methoxyethyl ether (0.092 g; 0.0009 mole) and azobisisobutyronitrile (0.01 g) were added to 2 g hexafluoroxylene and sealed under nitrogen in am ampoule. The solution was heated at 80° C. for 161/2 hours, then diluted with a further 4 g hexafluoroxylene. The polymer was precipitated by pouring the solution into some methanol. Filtration and drying gave 1.41 g (71% yield) of an off-white powder.

Elemental Analysis: Calc'd.: C, 29.82; H, 1.73; F, 59.33. Found: C, 29.47; H, 1.43; F, 60.82.

EXAMPLE 17 Copolymer of Example 16 Fumarate with Styrene

Following the procedure of Example 16, the polymerization was carried out with styrene (0.094 g; 0.0009 mole). The product was isolated in the manner described, yielding 1.37 g (68% yeild) of an off-white powder.

Elemental Analysis: Calc'd.: C, 31.42; H, 1.64; F, 58.27. Found: C, 31.38; H, 1.73; F, 58.18.

EXAMPLE 18 Homopolymer of 2,3-Bis(1,1,2,2-Tetrahydroperfluorodecylthio)Propyl Methacrylate

2,3-Bis(1,1,2,2-tetrahydroperfluorodecylthio)propyl methacrylate (2.00 g), dodecyl mercaptan (0.1 g) and azobisisobutyrinitrile (0.1 g) were added to 10 g hexafluoroxylene and sealed under nitrogen in an ampoule. The solution was heated at 80° C. for 17 hours, then diluted with a further 4 g hexafluoroxylene and then poured into 120 ml methanol. The precipitated polymer was washed and dried to give 1.69 g 80% yield) of a brittle, beige solid.

Elemental Analysis: Calc'd.: F, 54.02. Found: F, 54.19.

EXAMPLE 19

The utility of the polymers of the preceding Examples is illustrated in Table II. The materials were applied to the indicated fabrics at a loading of 0.12% fluorine on the treated fabric and tested for oil and water repellency by the methods already described.

                                      TABLE II                                     __________________________________________________________________________             Polyester Double Knit                                                                       65/35 Polyester/Cotton                                                                       100% Cotton Print                                                                            100% Wool                     luoropolymer                                                                          Oil                                                                               Rep.                                                                               Water Rep.                                                                            Oil                                                                               Rep.                                                                               Water Rep.                                                                            Oil                                                                               Rep.                                                                               Water Rep.                                                                            Oil                                                                               Rep.                                                                               Water Rep.             Example                                                                               A.sup.2                                                                           3M  A.sup.2                                                                               A.sup.2                                                                           3M  A.sup.2                                                                               A.sup.2                                                                           3M  A.sup.2                                                                               A.sup.2                                                                           3M  A.sup.2                __________________________________________________________________________     11     6  110 80                                                               12     6  110 90     5  100 70     5  100 50     8  140 100                    13     6  120 100                                                              14     6  120 100    5  110 50     5  90  50     8  140 100                    15     6  110 80                                                               16     6  110 90                                                               17     7  120 100                                                              18     3  80  90                                                               __________________________________________________________________________      A.sup.2 = AATCC oil rating or water spray test rating                          3M = 3M Oil Test                                                          

What is claimed is:
 1. A homopolymeric oil and water repellant compound consisting essentially of repeating units of the structure: ##STR30## wherein R¹, R² are each C_(n) H₂.sbsb.n, where n is 1 to 12 and may be straight chain or branched;R³ is hydrogen or C_(n) H₂.sbsb.n+1, where n is 1 to 12 and may be straight chain or branched; R⁴, r⁵ and R⁶ are hydrogen, methyl, ##STR31## provided that at least one of R⁴, R⁵ and R⁶ is hydrogen or methyl; R_(f) is C_(p) F_(2p+1) or C_(p) F_(2p+1) OC_(q) F_(2q), where p is 3 to 18, q is 2 to
 8. 2. A polymeric compound exhibiting oil and water repellent properties consisting essentially of a copolymer of(1) a polymerizable monomer having ethylenic unsatuation selected from the group consisting of ethylene and the chloro, fluoro and cyano substituted derivatives thereof; methacrylonitrile; hexafluoropropylene; acrylate and methacrylate esters, having from 1-18 carbon atoms in the ester group thereof; nitrogenvinyl monomers; dienes; styrenes; vinyl esters; alkyl vinyl ethers; and straight and branched α-olefins with up to 10 carbon atoms in the side chain thereof; and (2) a monomer of the structure ##STR32## wherein R¹, R² are each C_(n) H₂.sbsb.n, where n is 1 to 12 and may be straight chain or branched;R³ is hydrogen or C_(n) H₂.sbsb.n+1, where n is 1 to 12 and may be straight chain or branched; R⁴, r⁵ and R⁶ are hydrogen, methyl, ##STR33## provided that at least one of R⁴, R⁵ and R⁶ is hydrogen or methyl; R_(f) is C_(p) F_(2p+1) or C_(p) F_(2p+1) OC_(q) F_(sq) m where p is 3 to 18, and p is 2 to
 8. 3. A polymeric compound according to claim 2, wherein said polymerizable monomer having ethylenic unsaturation is selected from the group consisting of vinyl acetate, styrene, vinyl methyl ether, vinyl pyrrolidone and vinyl -2- methoxyethyl ether.
 4. A polymeric compound according to claim 3, wherein said polymerizable monomer having ethylenic unsaturation is vinyl methyl ether or vinyl pyrrolidone.
 5. The polymeric compound of claim 3, whereinR¹ is --CH₂ CH₂ --, R² is --CH₂ --, R³, r⁴ and R⁵ are hydrogen, and R⁶ is methyl.
 6. The polymeric compound of claim 3, whereinR¹ is --CH₂ CH₂ --, R² is --CH₂ --, R³ is hydrogen, R⁴ is ##STR34## and R⁵ and R⁶ are hydrogen.
 7. The polymeric compound of claim 3, whereinR¹ is --CH₂ CH₂ --, R² is --CH₂ --, R³, r⁴ and R⁵ are hydrogen, and R⁶ is ##STR35## 